Stainless Steel, Custom 465
This grade is a registered trademark of Carpenter Technology Corporation.
This alloy is a Martensitic Age Hardenable Stainless with exceptional tensile strength and corrosion resistance. The strength of this grade is superior to that of Custom 455.
The applications are generally used in the Aerospace and Defence Industries.
| Chemical Composition (Weight %) |
|||||||||||||||||
| C | Mn | Si | P | S | Cr | Ni | Mo | Ti | N | ||||||||
| Min | 11.00 | 10.75 | 0.75 | 1.50 | |||||||||||||
| Max | 0.02 | 0.25 | 0.25 | 0.015 | 0.01 | 12.50 | 11.25 | 1.25 | 1.80 | 0.01 | |||||||
| Typical Mechanical Properties (Min) | ||||||||||
| Condition | Tensile Strength, MPa | Yield Strength 0.2%, MPa | Elongation % | Reduction of Area % | Hardness HRC | |||||
| H950 | 1655 | 1515 | 10 | 45 | ||||||
| H1000 | 1515 | 1380 | 10 | 50 | ||||||
Related Specifications and Conditions
UNS S46500, AMS5936, ASTM A693, ASTM A564, 1.4614
Available Forms
Round bar, flat bar, billet, strip, wire, forgings
| Chemical Composition (Weight %) |
||||||||
| Min | Max | |||||||
| C | 0.02 | |||||||
| Mn | 0.25 | |||||||
| Si | 0.25 | |||||||
| P | 0.015 | |||||||
| S | 0.01 | |||||||
| Cr | 11.00 | 12.50 | ||||||
| Ni | 10.75 | 11.25 | ||||||
| Mo | 0.75 | 1.25 | ||||||
| Ti | 1.50 | 1.80 | ||||||
| N | 0.01 | |||||||
| Typical Mechanical Properties (Min) | |||||||
| Condition H950 | |||||||
| Tensile Strength, MPa | 1655 | ||||||
| Yield Strength 0.2%, MPa | 1515 | ||||||
| Elongation % | 10 | ||||||
| Reduction of Area % | 45 | ||||||
| Hardness HRC | |||||||
| H1000 | |||||||
| Tensile Strength, MPa | 1515 | ||||||
| Yield Strength 0.2%, MPa | 1380 | ||||||
| Elongation % | 10 | ||||||
| Reduction of Area % | 50 | ||||||
| Hardness HRC | |||||||
Related Specifications and Conditions
UNS S46500, AMS5936, ASTM A693, ASTM A564, 1.4614
Available Forms
Round bar, flat bar, billet, strip, wire, forgings