Stainless Steel, A286
This grade is an Iron based super alloy, which is known for its resistance to corrosion and retention of strength in elevated temperatures. The material is mainly used for machining and forming Gas Turbine, Steam Turbine and Aerospace Parts.
| Chemical Composition (Weight %) |
|||||||||||||||||
| C | Mn | Si | P | S | Cr | Ni | Mo | Ti | B | V | Co | Al | Cu | ||||
| Min | 13.50 | 24.00 | 1.00 | 1.90 | 0.003 | 0.10 | |||||||||||
| Max | 0.08 | 2.00 | 1.00 | 0.025 | 0.025 | 16.00 | 27.00 | 2.35 | 2.35 | 0.010 | 0.50 | 1.00 | 0.35 | 0.50 | |||
| Typical Mechanical Properties (Min) | ||||||||||
| Condition | Tensile Strength, KSI | Yield Strength 0.2%, KSI | Elongation % | Reduction of Area % | Hardness HB | |||||
| Sol Ann + aged | 130 | 85 | 15 | 20 | 248-341 | |||||
Related Specifications and Conditions
UNS S66286, AMS5525, AMS5731, AMS5732, AMS5734, AMS5737, AMS5853, AMS5858, AMS5895, ASTM A638, ASTM A453, BS HR51, BS HR52, BS HR650, 1.4980
Available Forms
Round bar, flat bar, hex bar, sheet, strip, plate, wire, coil, forgings
| Chemical Composition (Weight %) |
||||||||
| Min | Max | |||||||
| C | 0.08 | |||||||
| Mn | 2.00 | |||||||
| Si | 1.00 | |||||||
| P | 0.025 | |||||||
| S | 0.025 | |||||||
| Cr | 13.50 | 16.00 | ||||||
| Ni | 24.00 | 27.00 | ||||||
| Mo | 1.00 | 2.35 | ||||||
| Ti | 1.90 | 2.35 | ||||||
| B | 0.003 | 0.010 | ||||||
| V | 0.10 | 0.50 | ||||||
| Co | 1.00 | |||||||
| Al | 0.35 | |||||||
| Cu | 0.50 | |||||||
| Typical Mechanical Properties (Min) | |||||||
| Condition Sol Ann + aged | |||||||
| Tensile Strength, KSI | 130 | ||||||
| Yield Strength 0.2%, KSI | 85 | ||||||
| Elongation % | 15 | ||||||
| Reduction of Area % | 20 | ||||||
| Hardness HB | 248-341 | ||||||
Related Specifications and Conditions
UNS S66286, AMS5525, AMS5731, AMS5732, AMS5734, AMS5737, AMS5853, AMS5858, AMS5895, ASTM A638, ASTM A453, BS HR51, BS HR52, BS HR650, 1.4980
Available Forms
Round bar, flat bar, hex bar, sheet, strip, plate, wire, coil, forgings