Aluminium, 2014A Bar

Ti-3Al-2.4V has exceptional corrosion resistance and can be used in higher temperatures that Grade 1 through to Grade 4. The grade has many applications in Aerospace, Medical, Marine, Automotive, Transportation and Chemical Processing.

Chemical Composition (Weight %)
  Si Fe Cu Mn Mg Cr Ni Zn Ti Ti + Zr Al
Min 0.50
3.9 0.40  0.20






Max 0.90 0.50 5.0 1.2 0.8 0.10 0.10 0.25 0.15 0.20 Bal

Typical Mechanical Properties (Min)
Diameter or minor sectional dimension mm Tensile Strength, MPa Yield Strength 0.2%, MPa  Elongation %
0-2.5 415 370 6
2.5-10 435 385 6
10-25 460 415 7
25-75 490 440 7
75-100 480 435 7
100-150 465 420 7
150-200 435 390 7
 

Related Specifications and Conditions

L168-T6 solution treated, straightened and artificially aged,
L168-T651 solution treated controlled stretched and artificially aged,
L168-T6511 solution treated controlled stretched straightened and artificially aged

Available Forms 

Round bar, flat bar
 
Chemical Composition (Weight %)
  Min Max
Si 0.50 0.90
Fe   0.50
Cu 3.9 0.40 5.0
Mn 0.20 1.2
Mg   0.8
Cr   0.10
Ni   0.10
Zn   0.25
Ti   0.15
Ti + Zr   0.20
Al   Bal

Typical Mechanical Properties (Min)
Diameter or minor sectional dimension mm 0-2.5
Tensile Strength, MPa 415
Yield Strength 0.2%, MPa 370
 Elongation % 6
2.5-10
Tensile Strength, MPa 435
Yield Strength 0.2%, MPa 385
 Elongation % 6
10-25
Tensile Strength, MPa 460
Yield Strength 0.2%, MPa 415
 Elongation % 7
25-75
Tensile Strength, MPa 490
Yield Strength 0.2%, MPa 440
 Elongation % 7
75-100
Tensile Strength, MPa 480
Yield Strength 0.2%, MPa 435
 Elongation % 7
100-150
Tensile Strength, MPa 465
Yield Strength 0.2%, MPa 420
 Elongation % 7
150-200
Tensile Strength, MPa 435
Yield Strength 0.2%, MPa 390
 Elongation % 7
 

Related Specifications and Conditions

L168-T6 solution treated, straightened and artificially aged, L168-T651 solution treated controlled stretched and artificially aged, L168-T6511 solution treated controlled stretched straightened and artificially aged

Available Forms 

Round bar, flat bar, sheet, plate, strip, wire, forgings, tubes